On the Diffusion in Solids under Finite Deformation

ABSTRACT

The governing equations of diffusion in solids, undergoing finite deformation, are presented. Lagrangian and Eulerian descriptions are provided. The governing equations are particularly useful in cases of diffusion-driven degradation mechanisms ahead of cracks in metals, when crack tip blunting is not negligible. Emphasis is placed on hydrogeninduced embrittlement.